PrimaCreator Value UV / DLP Tough resin is suitable for 3D printing with UV and DLP printers that use a 395–405 nm light source. Printed and cured parts have ABS-like strength, are flexible and less brittle than standard cured resin parts, and can return to their original shape after bending. They have a matte surface, with fine detail and smooth transitions between layers.

This resin is used for prototyping, model making and the production of functional parts. After printing, parts are cleaned with PrimaCreator Resin Cleaner or IPA and cured in sunlight or in a UV chamber. The curing time is 4–12 seconds per 0.05 mm layer, while the bottom layer requires 40–60 seconds.

• Compatibility: PrimaCreator
• Color: Clear
• Capacity: 500 ml
• UV wavelength: 395–405 nm
• Curing time: 4–12 s per 0.05 mm layer
• Bottom layer curing time: 40–60 s
• Flexural modulus: 1,192–2,525 MPa
• Flexural strength: 60–80 MPa
• Coefficient of thermal expansion: 97*E-6
• Tensile strength: 42–62 MPa
• Tensile modulus: 1.86–2.645 MPa
• Elongation at break: 11%–21%
• Shore D hardness: 76–80
• Glass transition temperature: 70 ℃
• Density: 1.05–1.25 g/cm³
• Notched impact strength: 60–80 j/m
• Viscosity: 150–350 MPa·s