The Wanhao UV-DLP resin is particularly suitable for processing in DLP and UV LED 3D printers. Both 3D printing technologies use UV light sources to polymerize (solidify the resin through a chemical reaction) the liquid resin with the action of UV light at a wavelength of 405 nanometers.

The properties of this resin material include:

• Polymerizes with UV light at a wavelength of 405 nm
• High-energy UV light source is used for the curing of DLP and UV LED resin
• Fast polymerization process due to optimized resin
• Designed for use in Wanhao DLP and UV LED 3D printers

This resin can be processed in almost all DLP and UV LED 3D printers, but it is optimized for use in Wanhao printers.

Tips for optimal 3D printing results with Wanhao DLP resin:

• Clean your objects in an isopropyl alcohol bath after printing. Leave your parts in the isopropyl alcohol for about 10 minutes.
• The alcohol removes excess resin from your 3D prints. Allow the objects to air dry.
• Let the dry part cure under UV light until it reaches its final strength.
• As a UV light source, you can use UV LEDs or natural sunlight.

More information:

• Store in a cool, dark, and dry place
• Exposure time for material curing: 8 – 16 s
• Viscosity (at 25 °C): 120 to 140 mPa.s
• Material density (25 °C): 1.12 g/cm3
• Available packaging: 250 g / 500 g / 1000 g – 1 liter
• Curing depth of the materials: 0.1 mm
• Storage temperature: 8 ~ 28 °C
• Shelf life: 12 months
• Curing (horizontal): 79.2
• Shear (horizontal direction): 8.43 MPa
• Tensile strength (horizontal direction): 21.4 MPa
• Curing (vertical direction): 73.5
• Shear (vertical direction): 5.57 MPa
• Tensile strength (vertical direction): 15.2 MPa
• Solid content: 65.0% - 66.0% (testing temperature: 105 °C)
• Molecular weight: 1000-30000