Anycubic ABS-Like Resin Pro 2 is a photopolymer for LCD and DLP 3D printers, with an impact strength of up to 212 J/m and elongation at break of 35–40%. Its low volumetric shrinkage helps ensure accurate details and a smooth surface on printed models. Its formulation reduces odor during printing.

The material’s low viscosity and good flow make it easier to form successive layers, while its adhesion to the build plate helps reduce print failures. The resin can be used for structural components, handles, assembly fixtures, and industrial prototypes.

• Resin type: ABS-like photopolymer
• Color: Transparent
• Weight: 1 kg
• Compatibility: LCD and DLP 3D printers with 365–405 nm UV radiation
• Viscosity: 300–400 mPa·s at 25 °C
• Density: 1.05–1.25 g/cm³
• Hardness: 82–84 HD
• Tensile strength: 35–45 MPa
• Elongation at break: 35–40%
• Flexural modulus: 40–45 MPa
• Flexural strength: 1,400–1,800 MPa
• Young’s modulus: 1,600–1,800 MPa
• Izod impact strength: 212 J/m
• Volumetric shrinkage: 4.3–5.6%
• Printing temperature: 20–50 °C
• Recommended ambient printing temperature: 20–40 °C
• First-layer exposure time: 20–40 s
• Standard-layer exposure time: 1.5–3 s
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30 °C
• UV irradiance: 25,000–30,000 μW/cm²
• Curing time: 3 minutes