The Anycubic IPHTFBK-101 PETG-CF 3D printing filament is reinforced with carbon fibers, which provide increased stiffness and impact resistance compared with standard PETG. Its satin-matte surface conceals layer lines, while its low shrinkage helps ensure dimensional stability in prints.

The material is water- and weather-resistant, with heat resistance up to 100 °C. It is compatible with desktop printers and most spoolless filaments. The built-in chip enables automatic recognition by the Anycubic ACE Pro system, while the reusable threaded spool helps prevent tangling. A hardened steel nozzle is recommended.

• Material: PETG-CF with carbon fibers
• Color: Black
• Weight: 1 kg
• Compatibility: Anycubic ACE Pro, most spoolless filaments
• Recommended nozzle diameter: ≥ 0.4 mm
• Nozzle temperature: 240–270 °C
• Bed temperature: 65–75 °C
• Recommended printing speed: 40–250 mm/s
• Cooling time: 6 s
• Maximum flow rate: 11 mm³/s
• Density: 1.32 g/cm³
• Material flow rate: 14.1 ± 1.6 g/10 min (190 °C / 2.16 kg)
• Melting temperature: 221 °C
• Vicat softening temperature: 74 °C
• Heat deflection temperature: 67 °C (0.45 MPa)
• Water absorption: 0.38%
• Material stiffness (Young's modulus): 2550 ± 100 MPa
• Tensile strength: 54 ± 2 MPa
• Elongation at break: 12 ± 1%
• Impact strength (Izod): 3100 ± 150 MPa
• Flexural strength: 88 ± 2 MPa
• Izod impact strength (X-Y): 60 ± 4 kJ/m²
• Tensile strength (Z): 37 ± 3 MPa