Sting3d PLA Silk is a polymerized material composed of PLA with a special additive for lower melting temperature, intense gloss, and lower viscosity, facilitating the removal of supports. The molecular weight distribution is uniform, making the material's molecules more compatible, with consistent diameter and improved printing results.

Features:

• The material is composed of PLA ester compounds.
• The "silk" effect on the surface is noticeable.
• It withstands printing temperatures well, offering a good silk feel.

Packaging:

• 1kg / spool, 10 spools / box. Box size: 44*35*23cm
• Packaging: 1kg / spool + seal + box + storage bag with zipper

Filament Data:

• Physical Properties: Material Density: 1.21-1.30g/cm³ (GB/T1033.1-1986)
• Mechanical Properties: Breaking Stress: 17-18 (25um ASTM D1992), ≥50Mpa (GB/T1040-1992)
• Elongation at break: 4.6-5.3% (GB/T1040.1-1992)
• Impact Strength (KJ/M, Izod2): 1-3 (GB/T1043-1992)
• Thermal Properties: Vicat Softening Point: 61.5℃ (GB/T19466.2-2004)
• Melting index (g/10min): 4-6 (190 ℃, 2.15kg) (GB/T3682-2000)
• Melting point: 178.5 ℃ (GB/T19466-2004)
• Printing Properties: Printing Temperature: 190-220 ℃
• Bed Temperature: 0-40℃
• Airflow: off (Maximum 20%)