Anycubic ABS-Like 3.0 Resin is a photopolymer material for LCD and DLP 3D printers that use ultraviolet light with a wavelength of 365–405 nm. It has a tensile strength of 38–45 MPa, elongation at break of 25–30%, and impact strength of 130 J/m, while its volumetric shrinkage of 3.9–4.9% helps ensure precise detail reproduction and smooth model surfaces.

The material has a hardness of 83–86 HD and low warping tendency, making it suitable for mechanical parts, device housings, and automotive components. Its low odor and viscosity of 280–300 mPa·s make it easier to use, while its good flow properties can help reduce print times.

• Resin type: ABS-Like 3.0
• Material: Photopolymer resin
• Color: Gray
• Compatibility: LCD and DLP 3D printers
• Wavelength: 365–405 nm
• Viscosity: 280–300 mPa·s at 25 °C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1,500–2,000 MPa
• Young’s modulus: 1,300–1,700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50 °C
• Recommended ambient printing temperature: 20–40 °C
• Bottom layer exposure time: 23–40 seconds
• Normal layer exposure time: 2–3.6 seconds
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• Ultraviolet wavelength during curing: 405 nm
• Curing temperature: 18–30 °C
• Ultraviolet intensity: 25,000–30,000 µW/cm²
• Curing time: 3 minutes
• Weight: 1 kg