Anycubic ABS-Like 3.0 resin is a photopolymer material for LCD and DLP 3D printers, with a wavelength range of 365–405 nm. Its low shrinkage and viscosity help reproduce fine details and create a smooth surface, while its good flow helps reduce printing time. Its formulation has minimal odor, and its elongation at break reaches 30%.

The resin has an impact strength of 130 J/m and a hardness of 83–86 HD. It is intended for printing parts subject to stress, such as mechanical components and device housings, which can be drilled and further machined.

• Resin type: ABS-Like
• Color: Black
• Compatibility: LCD and DLP 3D printers using 365–405 nm ultraviolet light
• Material: Photopolymer resin
• Viscosity: 280–300 mPa·s at 25 °C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1500–2000 MPa
• Young's modulus: 1300–1700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50 °C
• Recommended ambient printing temperature: 20–40 °C
• First-layer exposure time: 23–40 s
• Standard-layer exposure time: 2–3.6 s
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30 °C
• UV irradiance: 25,000–30,000 μW/cm²
• Curing time: 3 minutes
• Weight: 1 kg